Stainless Steel 304

	Material Notes Type 304 stainless steel is a T 300 Series Stainless Steel austenitic. It has a minimum of 18% chromium and 8% nickel, combined with a maximum of 0.08% carbon. It is defined as a Chromium-Nickel austenitic alloy. Grade 304 is the standard "18/8" stainless that you will probably see in your pans and cookery tools.
	These are some of its characteristics: - Forming and welding properties - Corrosion/ oxidation resistance thanks to the chromium content - Deep drawing quality - Excellent toughness, even down to cryonegic temperatures which are defined as very low temperatures - Low temperature properties responding well to hardening by cold working - Ease of cleaning, ease of fabrication, beauty of appearance
	Grade 304L is the low carbon version of 304. It does not require post-weld annealing and so is extensively used in heavy gauge components (over about 6mm). Grade 304H with its higher carbon content finds application at elevated temperatures.
	Applications It is used for a wide variety of home and commercial applications, this is one of the most familiar and most frequently used alloys in the stainless steel family. Typical applications include tanks and containers for a large variety of liquids and solids:
	- Food industry Food processing equipment, particularly in beer brewing, milk processing & wine making. For example it is highly suitable and applied in dairy equipment such as milking machines, containers, homogenizers, sterilizers, and storage and hauling tanks, including piping, valves, milk trucks and railroad cars.
	Very common in the brewing industry where it is used in pipelines, yeast pans, fermentation vats, storage and railway cars, etc. The citrus and fruit juice industry also uses Type 304 for all their handling, crushing, preparation, storage and hauling equipment.
	- Domestic tools industry Because of its ability to withstand the corrosive action of various acids found in fruits, meats, milk, and vegetables, Type 304 is used for sinks, tabletops, coffee urns, stoves, refrigerators, milk and cream dispensers, and steam tables. It is also used in numerous other utensils such as cooking appliances, pots, pans, and flatware.
	- Architectural panelling, railings & trim - Chemical containers, including for transport - Heat Exchangers - Woven or welded screens for mining, quarrying & water filtration - Dyeing industry - In the marine environment, because of it slightly higher strength and wear resistance than type 316 it is also used for nuts, bolts, screws, and other fasteners.

Chemistry % by Weight

Element
	Type 302	Type 304	Type 304L	Type 305

Fe	64.99-74%
Cr	17%	18%	18%	17%
Ni	8%	8%	8%	10.50%
Mn	2%	2%	2%	2%
N	0.10%	0.10%	0.10%	-
S	0.03%	0.03%	0.03%	0.03%
C	0.15%	0.08%	0.03%	0.12%
Si	0.75%	0.75%	0.75%	0.75%
P	0.045%	0.045%	0.045%	0.045%

Possible Alternative Grades

Possible alternative grades to 304 grade stainless steel:

- Grade 301L: It is applicable for higher work hardening rate grade.
It could be required for certain roll formed or stretch formed components.

- Grade 302HQ: Lower work hardening rate grade. It could be needed for cold forging of screws, bolts and rivets.

- Grade 303: Higher machinability needed; lower corrosion resistance; acceptable formability and weldability.

- Grade 316: Used when higher resistance to pitting and crevice corrosion is required, also in chloride environments

- Grade 321: Better resistance to temperatures of around 600-900°C. It has higher hot strength.

- Grade 3CR12: It has lower cost; reduced corrosion resistance and resulting discoloration are acceptable.

- Grade 430: It has lower cost; reduced corrosion resistance and fabrication characteristics are acceptable.

Properties
Properties	Value	Comment
Physical Properties
Density	8.03 g/cc
Mechanical properties
Hardness, Rockwell B	82
Tensile Strength, Ultimate	621 Mpa (=90100psi)
Tensile Strength, Yield	290 Mpa (=42100psi)	0.2% YS
Elongation at Break	55%	in 2 inches
Modulus of Elasticity	193 Gpa	tension
Modulus of Elasticity	78 Gpa	torsion
Electrical properties
Electrical Resistivity	0.000116 ohm-cm	659 °C
Electrical Resistivity	7.2e-005 ohm-cm
Magenetic permeability	Max 1.02	H = 200 Oersteds, Annealed
Thermal properties
CTE, linear 20°C	16.9 µm/m-°C	0 to 100°C
CTE, linear 20°C	18.7 µm/m-°C	to 649°C
Heat Capacity	0.5 J/g-°C	0°C to 100°
Thermal Conductivity	16.2 W/m-K	100°C
Thermal Conductivity	21.4 W/m-K	500°C
Processing properties
Melt temperature	1371- 1399 °C

For information about the periodic table of elements

Stainless steel 316

Stainless steel general information

About Lenntech

Lenntech (European Head Office)

Distributieweg 3
2645 EG Delfgauw
The Netherlands
Phone: +31 152 610 900
fax: +31 152 616 289
e-mail: info@lenntech.com

Lenntech USA LLC (Americas)

5975 Sunset Drive
South Miami, FL 33143
USA
Phone: +1 877 453 8095
e-mail: info@lenntech.com

Lenntech DMCC (Middle East)

Level 6 - OFFICE #101-One JLT Tower
Jumeirah Lake Towers
Dubai - U.A.E.
Phone: +971 4 429 5853
e-mail: info@lenntech.com

General Delivery Conditions