Nickel electroplating is a technique of electroplating a thin layer of nickel onto a metal object. The nickel layer can be decorative, provide corrosion resistance, wear resistance, or used to build up worn or undersized parts for salvage purposes.[1][2]

Overview edit

Nickel electroplating is a process of depositing nickel onto a metal part. Parts to be plated must be clean and free of dirt, corrosion, and defects before plating can begin.[3] To clean and protect the part during the plating process, a combination of heat treating, cleaning, masking, pickling, and etching may be used.[1] Once the piece has been prepared it is immersed into an electrolyte solution and is used as the cathode. The nickel anode is dissolved into the electrolyte to form nickel ions (Ni2+). Just like in other electrodeposition processes, the ions travel through the solution and deposit on the cathode.[4][5]

The anode efficiency for nickel dissolution is close to 100%, unless due to problems with the process anode becomes passive (and its efficiency thus 0). The cathode efficiency depends on the process and varies between 90 and 97%. Due to this mismatch, during the plating the nickel concentration in the solution and the pH will slowly rise.[6] The process takes minutes to hours depending on the current density and the intended thickness of the plating.[7]

History edit

The nickel electroplating was developed in the first half of the 19th century, with notable experiments made by Golding Bird (1837) and nickel nitrate patent by Joseph Shore (1840). The first practical recipe, an aqueous solution of nickel and ammonium sulfates, was invented by Böttger in 1843 and was in use for 70 years.[8] The commercial success was achieved by Isaac Adams Jr., whose patent for a solution of nickel ammonium sulfate, while similar to Böttger's, had neutral pH that made the process easier to control. Adams enjoyed a near-monopoly in nickel plating from 1869 to 1886, when the consumption of nickel for plating reached 135 tons.[4] In the US, Remington tried to use the nickel ammonium chloride solution (1868), in the process establishing the anode construction in the form of a platinum basket filled with nickel pieces,[4] Edward Weston initiated the use of boric acid (patent issued in 1878),[9] Bancroft figured out the role of chlorides in dissolving the anode (1906).[4][10] Finally, Oliver P. Watts in 1916 established the Watts bath, variations of which are still widely used for decorative plating, with sulfamate solutions challenging it in the engineering applications.[4]

Types and chemistry edit

Watts baths edit

A Watts bath, named for its inventor Oliver Patterson Watts, is an aqueous electrolyte solution for plating nickel from a nickel anode. It can deposit both bright and semi-bright nickel. Bright nickel is typically used for decorative purposes and corrosion protection. Semi-bright deposits are used for engineering applications where high corrosion resistance, ductility or electrical conductivity is important, and a high luster is not required.[2][11][12]

Bath composition edit

Chemical Name Formula Bright[11] Semi-bright[11]
Metric US Metric US
Nickel sulfate NiSO4·6H2O 150–300 g/L 20–40 oz/gal 225–300 g/L 30–40 oz/gal
Nickel chloride NiCl2·6H2O 60–150 g/L 8–20 oz/gal 30–45 g/L 4–6 oz/gal
Boric acid H3BO3 37–52 g/L 5–7 oz/gal 37–52 g/L 5–7 oz/gal

Operating conditions edit

  • Temperature: 40-65 °C
  • Cathode current density: 2-10 A/dm2
  • pH: 4.5-5

Brighteners edit

  • Carrier brighteners (e.g. paratoluene sulfonamide, benzene sulphonic acid) in concentration 0.75-23 g/L. Carrier brighteners contain sulfur providing uniform fine grain structure of the nickel plating.[5]
  • Levelers, second class brighteners (e.g. allyl sulfonic acid, formaldehyde chloral hydrate) in concentration 0.0045-0.15 g/L produce (in combination with carrier brighteners) brilliant deposit.[5]
  • Auxiliary brighteners (e.g. sodium allyl sulfonate, pyridinium propyl sulfonate) in concentration 0.075-3.8 g/L.[5]
  • Inorganic brighteners (e.g. cobalt, zinc) in concentration 0.075-3.8 g/L. Inorganic brighteners impart additional lustre to the coating.[5]

Type of the added brighteners and their concentrations determine the deposit appearance: brilliant, bright, semi-bright, satin.

Nickel sulfamate edit

Sulfamate nickel plating is used for many engineering applications. It is deposited for dimensional corrections, abrasion and wear resistance, high efficiency coating and corrosion protection. It is also used as an undercoat for chromium.[2][13]

Bath composition edit

Chemical name Formula Bath concentration[5]
Metric US
Nickel sulfamate Ni(SO3NH2)2 300-450 g/L 40–60 oz/gal
Nickel chloride NiCl2·6H2O 0-30 g/L 0–4 oz/gal
Boric acid H3BO3 30-45 g/L 4–6 oz/gal

Operating conditions edit

  • Temperature: 40-60 °C[5]
  • Cathode current density: 2-25 A/dm2[5]
  • pH: 3.5-4.5[5]

All-chloride edit

All-chloride solutions allow for the deposition of thick nickel coatings. They do this because they run at low voltages. However, the deposition has high internal stresses.[2][5]

Chemical name Formula Bath concentration[5]
Nickel chloride NiCl2·6H2O 30–40 oz/gal
Boric acid H3BO3 4–4.7 oz/gal

Sulfate-chloride edit

A sulfate-chloride bath operates at lower voltages than a Watts bath and provide a higher rate of deposition. Although internal stresses are higher than the Watts bath, they are lower than that of an all-chloride bath.[2][5]

Chemical name Formula Bath concentration[5]
Nickel sulfate NiSO4·6H2O 20–30 oz/gal
Nickel chloride NiCl2·6H2O 20–30 oz/gal
Boric acid H3BO3 4–6 oz/gal

All-sulfate edit

An all-sulfate solution is used for electro-depositing nickel where the anodes are insoluble. For example, plating the insides of steel pipes and fittings may require an insoluble anode.[2][12]

Chemical name Formula Bath concentration[5]
Nickel sulfate NiSO4·6H2O 30–53 oz/gal
Boric acid H3BO3 4–6 oz/gal

Hard nickel edit

A hard nickel solution is used when a high tensile strength and hardness deposit is required.[2][5]

Chemical name Formula Bath concentration[5] Metric
Nickel sulfate NiSO4·6H2O 24 oz/gal 179.7g/L
Ammonium chloride NH4Cl 3.3 oz/gal 24.7 g/L
Boric acid H3BO3 4 oz/gal 29.96 g/L

Black nickel edit

"Black nickel" is a dark coating that consists primarily of nickel sulfide and metallic zinc and nickel.[14] It is typically plated on brass, bronze, or steel in order to produce a non-reflective surface.[15] This type of plating is used for decorative and military purposes and does not offer much protection.[1][2][15]

Chemical name Formula Bath concentration[15]
Nickel ammonium sulfate NiSO4·(NH4)2SO4·6H2O 8 oz/gal
Zinc sulfate ZnSO4 1.0 oz/gal
Sodium thiocyanate NaCNS 2 oz/gal

Applications edit

Decorative coating edit

Decorative bright nickel is used in a wide range of applications. It offers a high luster finish, corrosion protection, and wear resistance. In the automotive industry bright nickel can be found on bumpers, rims, exhaust pipes and trim. It is also used for bright work on bicycles and motorcycles. Other applications include hand tools and household items such as lighting and plumbing fixtures, wire racks, firearms, and appliances.[11]

Modern coating technology makes deposited nickel to appear mirror-bright with no need of polishing, multi-layer applications are frequently used to improve the corrosion resistance of coated steel, zinc, copper, aluminum, and other metals. In order to prevent tarnishing, decorative electroplated nickel is typically coated with a thin layer of chromium.[8]

Engineering applications edit

Engineering nickel is used where brightness is not desired. Non decorative applications provide wear and corrosion protection as well as low-stress buildups for dimensional recovery,[11][16] nickel or its nickel alloys usually having matte or dull finish.[8] The method can be used for making nanocomposite wear resistance coatings.[17][18]

Nickel electroforming has nickel plating applied for fabrication of nickel products. For example, nickel can be deposited onto a mandrel and then lifted off the latter, creating a nickel-only part.[8]

See also edit

References edit

  1. ^ a b c "QQ-N-290 A NICKEL PLATING". www.everyspec.com. Retrieved 2018-02-25.
  2. ^ a b c d e f g h Ian Rose; Clive Whittington; William Lo (2022). "Nickel Plating Handbook" (PDF). Nickel Institute.
  3. ^ "MIL-P-27418 PLATING SOFT NICKEL ELECTRO-DEPOSITED BATH". www.everyspec.com. Retrieved 2018-02-25.
  4. ^ a b c d e Di Bari 2011, p. 80.
  5. ^ a b c d e f g h i j k l m n o p "Nickel electroplating [SubsTech]". www.substech.com. Retrieved 2018-02-25.
  6. ^ Di Bari 2011, p. 81.
  7. ^ Di Bari 2011, p. 82.
  8. ^ a b c d Di Bari 2011, p. 79.
  9. ^ Dubpernell 1959, p. 39.
  10. ^ Dubpernell 1959, p. 40.
  11. ^ a b c d e Snyder, Dr. Donald. "Nickel Electroplating". www.pfonline.com. Retrieved 2018-02-25.
  12. ^ a b "NickelElectroplating.pdf" (PDF). Retrieved 25 February 2018.
  13. ^ "We'll find the optimal approach to coating your parts. No one can beat Bales' wide array of engineered coatings and finishes".
  14. ^ Ibrahim, Magdy A. M. (2005). "Black nickel electrodeposition from a modified Watts bath". Journal of Applied Electrochemistry. 36 (3): 295–301. doi:10.1007/s10800-005-9077-8. ISSN 0021-891X. S2CID 95324802.
  15. ^ a b c "MIL-P-18317 PLATING BLACK NICKEL ON BRASS BRONZE OR". www.everyspec.com. Retrieved 2018-02-25.
  16. ^ Davis, Joseph R. (2000-01-01). Nickel, Cobalt, and Their Alloys. ASM International. ISBN 9780871706850. Retrieved 9 August 2016.
  17. ^ Mosallanejad, M. H.; Shafyei, A.; Akhavan, S. (18 April 2016). "Simultaneous co-deposition of SiC and CNT into the Ni coating". Canadian Metallurgical Quarterly. 55 (2): 147–155. Bibcode:2016CaMQ...55..147M. doi:10.1080/00084433.2016.1150406. S2CID 138392838. Retrieved 9 August 2016.
  18. ^ Zhang, Sam (2010-06-18). Nanostructured Thin Films and Coatings: Mechanical Properties. Taylor & Francis. ISBN 9781420094022. Retrieved 9 August 2016.

Sources edit